ENTRY O0339 19970516 0000O033900000001 SUBENT O0339001 19970516 0000O033900100001 BIB 15 48 O033900100002 TITLE Investigation of Aluminium,Titanium and Iron StructuralO033900100003 Materials Activation Using 1.0-1.3 GeV Protons. O033900100004 AUTHOR (V.S.BARASHENKOV,A.V.VOLCHANSKY,L.N.KONDRAT'EV, O033900100005 N.N.POMELOV,V.YU.RUSINOV,A.N.SOSNIN,P.I.TARANENKO, O033900100006 S.N.FEDOTOV) O033900100007 INSTITUTE (4ZZZDUB) O033900100008 (4RUSMIF) O033900100009 (4RUSITE) O033900100010 REFERENCE (J,NIM/A,292,169,90) O033900100011 HISTORY (970506C) O033900100012 (970516U) Last checking has been done. O033900100013 SAMPLE Al,Ti and Fe Targets Formed As a Parallelepiped 6*6 O033900100014 Cm**2.The Target was Composed of Separated Plates of O033900100015 1-10 mm Thickness,Which Allowed the Study of the O033900100016 Distribution of Nuclear Reaction Products Near the O033900100017 Target Depth. O033900100018 ADD-RES (COMP).Cascade Program. O033900100019 The Gamma-Radiation Spectrum from the Ti and Fe TargetsO033900100020 At E(P)=1.1 GeV was Reported. O033900100021 DETECTOR (TELES).The Proton Beam Monitoring has Been Carried OutO033900100022 With the Help of a Telescope, Consisting of Three O033900100023 Counters Working in a Coincidence Mode. O033900100024 (GELI) O033900100025 FACILITY (SYNCY,4RUSITE) O033900100026 MISC-COL (MISC).Authors' Data in Units-10E-04*Gramm**(-1)*Cm**2 O033900100027 Per One Incident Proton. O033900100028 (MISC-ERR).'Misc' Uncertainty. O033900100029 COMMENT /by Compiler/. O033900100030 1. The Authors Data were Recalculated by CompilerO033900100031 Using Formula- Sigma=(Y*E-04*A(I))/(P(I)*N(A)) *E+27, O033900100032 Where Y-Authors Data, O033900100033 P(I)-Target Thickness, O033900100034 N(A)-Avagadro Number, O033900100035 A(I)-Atomic Weight of Target Nuclei. O033900100036 2. I would Like to Remark That Authors' Data are Less O033900100037 Than Another Investigations Data. O033900100038 3. The Authors did not Include any Correction For O033900100039 Secondary Particles Influence. They would Like to O033900100040 Measure Total Yield of the Activities. O033900100041 4. The Authors did not Remark Cumulative or IndependentO033900100042 Production Cases. O033900100043 METHOD (ACTIV) Each Sample has Been Exposed 8 to 10 Times. O033900100044 Minimum Cooling Time Reached 3-5 Minutes, Maximum Up toO033900100045 Two Days at Exposure Time from 5 Minutes to 2 Hours. O033900100046 (GSPEC) O033900100047 ANALYSIS (DECAY) O033900100048 REL-REF (R,,U.REUS+,J,AND,29,183,83) Decay-Data. O033900100049 STATUS (TABLE) O033900100050 ENDBIB 48 0 O033900100051 NOCOMMON 0 0 O033900100052 ENDSUBENT 51 0 O033900199999 SUBENT O0339002 19970516 0000O033900200001 BIB 6 9 O033900200002 REACTION (13-AL-27(P,X)12-MG-27,,SIG,,,EXP) O033900200003 COMMENT - By Compiler - 27-Mg Could not be Produced in this O033900200004 Reaction. 27-Mg Observation is Result of Secondary O033900200005 Neutrons Influence or a Admixture in Target. O033900200006 SAMPLE Aluminium, Thickness 13.5 G/Cm**2, was Used. O033900200007 RAD-DET (12-MG-27,DG) O033900200008 DECAY-DATA (12-MG-27,9.46MIN,DG,843.7,0.718, O033900200009 DG,1014.4,0.282) O033900200010 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033900200011 ENDBIB 9 0 O033900200012 NOCOMMON 0 0 O033900200013 DATA 5 1 O033900200014 EN DATA ERR-T MISC MISC-ERR O033900200015 GEV MB MB SEE TEXT SEE TEXT O033900200016 1.1 0.32 0.06 0.98 0.19 O033900200017 ENDDATA 3 0 O033900200018 ENDSUBENT 17 0 O033900299999 SUBENT O0339003 19970516 0000O033900300001 BIB 5 6 O033900300002 REACTION (13-AL-27(P,X)11-NA-24,CUM,SIG,,,EXP) O033900300003 SAMPLE Aluminium,Thickness 13.5 G/Cm**2,was Used. O033900300004 RAD-DET (11-NA-24,DG) O033900300005 DECAY-DATA (11-NA-24,15.02HR,DG,1368.5,1., O033900300006 DG,2753.9,0.999) O033900300007 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033900300008 ENDBIB 6 0 O033900300009 NOCOMMON 0 0 O033900300010 DATA 5 1 O033900300011 EN DATA ERR-T MISC MISC-ERR O033900300012 GEV MB MB SEE TEXT SEE TEXT O033900300013 1.1 0.83 0.06 2.53 0.18 O033900300014 ENDDATA 3 0 O033900300015 ENDSUBENT 14 0 O033900399999 SUBENT O0339004 19970516 0000O033900400001 BIB 5 5 O033900400002 REACTION (22-TI-0(P,X)21-SC-48,,SIG,,,EXP) Independent O033900400003 SAMPLE Titanium, Thickness 4.54 G/Cm**2,was Used. O033900400004 RAD-DET (21-SC-48,DG) O033900400005 DECAY-DATA (21-SC-48,1.82D,DG,1037.5,0.975) O033900400006 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033900400007 ENDBIB 5 0 O033900400008 NOCOMMON 0 0 O033900400009 DATA 5 1 O033900400010 EN DATA ERR-T MISC MISC-ERR O033900400011 GEV MB MB SEE TEXT SEE TEXT O033900400012 1.1 0.74 0.21 0.42 0.12 O033900400013 ENDDATA 3 0 O033900400014 ENDSUBENT 13 0 O033900499999 SUBENT O0339005 19970516 0000O033900500001 BIB 5 5 O033900500002 REACTION (22-TI-0(P,X)23-V-48,IND,SIG,,,EXP) O033900500003 SAMPLE Titanium,Thickness 4.54 G/Cm**2,was Used. O033900500004 RAD-DET (23-V-48,DG) O033900500005 DECAY-DATA (23-V-48,15.97D,DG,983.5,1.) O033900500006 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033900500007 ENDBIB 5 0 O033900500008 NOCOMMON 0 0 O033900500009 DATA 5 1 O033900500010 EN DATA ERR-T MISC MISC-ERR O033900500011 GEV MB MB SEE TEXT SEE TEXT O033900500012 1.1 0.3 0.05 0.17 0.03 O033900500013 ENDDATA 3 0 O033900500014 ENDSUBENT 13 0 O033900599999 SUBENT O0339006 19970516 0000O033900600001 BIB 5 5 O033900600002 REACTION (22-TI-0(P,X)21-SC-47,CUM,SIG,,,EXP) O033900600003 SAMPLE Titanium, Thickness 4.54 G/Cm**2,was Used. O033900600004 RAD-DET (21-SC-47,DG) O033900600005 DECAY-DATA (21-SC-47,3.34D,DG,159.4,0.68) O033900600006 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033900600007 ENDBIB 5 0 O033900600008 NOCOMMON 0 0 O033900600009 DATA 5 1 O033900600010 EN DATA ERR-T MISC MISC-ERR O033900600011 GEV MB MB SEE TEXT SEE TEXT O033900600012 1.1 7.04 0.56 4.02 0.32 O033900600013 ENDDATA 3 0 O033900600014 ENDSUBENT 13 0 O033900699999 SUBENT O0339007 19970516 0000O033900700001 BIB 5 5 O033900700002 REACTION (22-TI-0(P,X)21-SC-46-G,M+,SIG,,,EXP) Independent O033900700003 SAMPLE Titanium, Thickness 4.54 G/Cm**2,was Used. O033900700004 RAD-DET (21-SC-46-G,DG) O033900700005 DECAY-DATA (21-SC-46-G,83.8D,DG,889.2,1.) O033900700006 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033900700007 ENDBIB 5 0 O033900700008 NOCOMMON 0 0 O033900700009 DATA 5 1 O033900700010 EN DATA ERR-T MISC MISC-ERR O033900700011 GEV MB MB SEE TEXT SEE TEXT O033900700012 1.1 3.9 1.17 2.23 0.67 O033900700013 ENDDATA 3 0 O033900700014 ENDSUBENT 13 0 O033900799999 SUBENT O0339008 19970516 0000O033900800001 BIB 5 5 O033900800002 REACTION (22-TI-0(P,X)19-K-45,CUM,SIG,,,EXP) O033900800003 SAMPLE Titanium, Thickness 4.54 G/Cm**2,was Used. O033900800004 RAD-DET (19-K-45,DG) O033900800005 DECAY-DATA (19-K-45,17.8MIN,DG,174.3,0.753) O033900800006 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033900800007 ENDBIB 5 0 O033900800008 NOCOMMON 0 0 O033900800009 DATA 5 1 O033900800010 EN DATA ERR-T MISC MISC-ERR O033900800011 GEV MB MB SEE TEXT SEE TEXT O033900800012 1.1 0.12 0.04 0.068 0.024 O033900800013 ENDDATA 3 0 O033900800014 ENDSUBENT 13 0 O033900899999 SUBENT O0339009 19970516 0000O033900900001 BIB 5 7 O033900900002 REACTION (22-TI-0(P,X)21-SC-44-G,IND/(M),SIG,,,EXP) O033900900003 44-G-Sc Production Due to Radioactive Decay is O033900900004 Negligible As 44-Ti Half-Life is Equal 49 Years. O033900900005 SAMPLE Titanium, Thickness 4.54 G/Cm**2,was Used. O033900900006 RAD-DET (21-SC-44-G,DG) O033900900007 DECAY-DATA (21-SC-44-G,3.93HR,DG,1157.,0.999) O033900900008 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033900900009 ENDBIB 7 0 O033900900010 NOCOMMON 0 0 O033900900011 DATA 5 1 O033900900012 EN DATA ERR-T MISC MISC-ERR O033900900013 GEV MB MB SEE TEXT SEE TEXT O033900900014 1.1 2.24 0.26 1.28 0.15 O033900900015 ENDDATA 3 0 O033900900016 ENDSUBENT 15 0 O033900999999 SUBENT O0339010 19970516 0000O033901000001 BIB 5 5 O033901000002 REACTION (22-TI-0(P,X)21-SC-44-M,IND,SIG,,,EXP) O033901000003 SAMPLE Titanium, Thickness 4.54 G/Cm**2,was Used. O033901000004 RAD-DET (21-SC-44-M,DG) O033901000005 DECAY-DATA (21-SC-44-M,2.44D,DG,271.2,0.778) O033901000006 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033901000007 ENDBIB 5 0 O033901000008 NOCOMMON 0 0 O033901000009 DATA 5 1 O033901000010 EN DATA ERR-T MISC MISC-ERR O033901000011 GEV MB MB SEE TEXT SEE TEXT O033901000012 1.1 1.31 0.18 0.75 0.1 O033901000013 ENDDATA 3 0 O033901000014 ENDSUBENT 13 0 O033901099999 SUBENT O0339011 19970516 0000O033901100001 BIB 5 5 O033901100002 REACTION (22-TI-0(P,X)19-K-43,CUM,SIG,,,EXP) O033901100003 SAMPLE Titanium, Thickness 4.54 G/Cm**2,was Used. O033901100004 RAD-DET (19-K-43,DG) O033901100005 DECAY-DATA (19-K-43,22.3HR,DG,617.5,0.783) O033901100006 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033901100007 ENDBIB 5 0 O033901100008 NOCOMMON 0 0 O033901100009 DATA 5 1 O033901100010 EN DATA ERR-T MISC MISC-ERR O033901100011 GEV MB MB SEE TEXT SEE TEXT O033901100012 1.1 0.75 0.09 0.43 0.05 O033901100013 ENDDATA 3 0 O033901100014 ENDSUBENT 13 0 O033901199999 SUBENT O0339012 19970516 0000O033901200001 BIB 5 5 O033901200002 REACTION (22-TI-0(P,X)21-SC-43,CUM,SIG,,,EXP) O033901200003 SAMPLE Titanium, Thickness 4.54 G/Cm**2,was Used. O033901200004 RAD-DET (21-SC-43,DG) O033901200005 DECAY-DATA (21-SC-43,3.89HR,DG,372.8,0.225) O033901200006 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033901200007 ENDBIB 5 0 O033901200008 NOCOMMON 0 0 O033901200009 DATA 5 1 O033901200010 EN DATA ERR-T MISC MISC-ERR O033901200011 GEV MB MB SEE TEXT SEE TEXT O033901200012 1.1 0.77 0.07 0.44 0.04 O033901200013 ENDDATA 3 0 O033901200014 ENDSUBENT 13 0 O033901299999 SUBENT O0339013 19970516 0000O033901300001 BIB 5 7 O033901300002 REACTION (22-TI-0(P,X)19-K-42,IND,SIG,,,EXP) O033901300003 42-K Production Due to Radioactive Decay of 42-Ar is O033901300004 Negligible As 42-Ar Half-Life is Equal 33 Years. O033901300005 SAMPLE Titanium, Thickness 4.54 G/Cm**2,was Used. O033901300006 RAD-DET (19-K-42,DG) O033901300007 DECAY-DATA (19-K-42,12.36HR,DG,1524.6,0.183) O033901300008 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033901300009 ENDBIB 7 0 O033901300010 NOCOMMON 0 0 O033901300011 DATA 5 1 O033901300012 EN DATA ERR-T MISC MISC-ERR O033901300013 GEV MB MB SEE TEXT SEE TEXT O033901300014 1.1 1.96 0.39 1.12 0.22 O033901300015 ENDDATA 3 0 O033901300016 ENDSUBENT 15 0 O033901399999 SUBENT O0339014 19970516 0000O033901400001 BIB 5 5 O033901400002 REACTION (22-TI-0(P,X)18-AR-41,CUM,SIG,,,EXP) O033901400003 SAMPLE Titanium, Thickness 4.54 G/Cm**2,was Used. O033901400004 RAD-DET (18-AR-41,DG) O033901400005 DECAY-DATA (18-AR-41,1.83HR,DG,1293.7,0.991) O033901400006 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033901400007 ENDBIB 5 0 O033901400008 NOCOMMON 0 0 O033901400009 DATA 5 1 O033901400010 EN DATA ERR-T MISC MISC-ERR O033901400011 GEV MB MB SEE TEXT SEE TEXT O033901400012 1.1 0.35 0.05 0.2 0.03 O033901400013 ENDDATA 3 0 O033901400014 ENDSUBENT 13 0 O033901499999 SUBENT O0339015 19970516 0000O033901500001 BIB 5 5 O033901500002 REACTION (22-TI-0(P,X)17-CL-39,CUM,SIG,,,EXP) O033901500003 SAMPLE Titanium, Thickness 4.54 G/Cm**2,was Used. O033901500004 RAD-DET (17-CL-39,DG) O033901500005 DECAY-DATA (17-CL-39,55.6MIN,DG,250.2,0.463) O033901500006 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033901500007 ENDBIB 5 0 O033901500008 NOCOMMON 0 0 O033901500009 DATA 5 1 O033901500010 EN DATA ERR-T MISC MISC-ERR O033901500011 GEV MB MB SEE TEXT SEE TEXT O033901500012 1.1 0.21 0.05 0.12 0.03 O033901500013 ENDDATA 3 0 O033901500014 ENDSUBENT 13 0 O033901599999 SUBENT O0339016 19970516 0000O033901600001 BIB 5 5 O033901600002 REACTION (22-TI-0(P,X)16-S-38,CUM,SIG,,,EXP) O033901600003 SAMPLE Titanium, Thickness 4.54 G/Cm**2,was Used. O033901600004 RAD-DET (16-S-38,DG) O033901600005 DECAY-DATA (16-S-38,2.84HR,DG,1642.4,0.404) O033901600006 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033901600007 ENDBIB 5 0 O033901600008 NOCOMMON 0 0 O033901600009 DATA 5 1 O033901600010 EN DATA ERR-T MISC MISC-ERR O033901600011 GEV MB MB SEE TEXT SEE TEXT O033901600012 1.1 0.18 0.05 0.1 0.03 O033901600013 ENDDATA 3 0 O033901600014 ENDSUBENT 13 0 O033901699999 SUBENT O0339017 19970516 0000O033901700001 BIB 5 7 O033901700002 REACTION (22-TI-0(P,X)17-CL-38-G,(CUM),SIG,,,EXP) O033901700003 Any Information For Possible Influence of 38-S Decay onO033901700004 Production Cross Section is Absent. O033901700005 SAMPLE Titanium, Thickness 4.54 G/Cm**2,was Used. O033901700006 RAD-DET (17-CL-38-G,DG) O033901700007 DECAY-DATA (17-CL-38-G,37.24MIN,DG,1642.4,0.316) O033901700008 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033901700009 ENDBIB 7 0 O033901700010 NOCOMMON 0 0 O033901700011 DATA 5 1 O033901700012 EN DATA ERR-T MISC MISC-ERR O033901700013 GEV MB MB SEE TEXT SEE TEXT O033901700014 1.1 0.4 0.12 0.23 0.07 O033901700015 ENDDATA 3 0 O033901700016 ENDSUBENT 15 0 O033901799999 SUBENT O0339018 19970516 0000O033901800001 BIB 5 7 O033901800002 REACTION (22-TI-0(P,X)17-CL-34-M,IND,SIG,,,EXP) O033901800003 Radioactive Decay of 34-Ar to Isomer State of 34-Cl is O033901800004 Absent. O033901800005 SAMPLE Titanium, Thickness 4.54 G/Cm**2,was Used. O033901800006 RAD-DET (17-CL-34-M,DG) O033901800007 DECAY-DATA (17-CL-34-M,32.06MIN,DG,2127.3,0.432) O033901800008 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033901800009 ENDBIB 7 0 O033901800010 NOCOMMON 0 0 O033901800011 DATA 5 1 O033901800012 EN DATA ERR-T MISC MISC-ERR O033901800013 GEV MB MB SEE TEXT SEE TEXT O033901800014 1.1 0.32 0.09 0.18 0.05 O033901800015 ENDDATA 3 0 O033901800016 ENDSUBENT 15 0 O033901899999 SUBENT O0339019 19970516 0000O033901900001 BIB 5 5 O033901900002 REACTION (22-TI-0(P,X)13-AL-29,CUM,SIG,,,EXP) O033901900003 SAMPLE Titanium, Thickness 4.54 G/Cm**2,was Used. O033901900004 RAD-DET (13-AL-29,DG) O033901900005 DECAY-DATA (13-AL-29,6.52MIN,DG,1273.3,0.906) O033901900006 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033901900007 ENDBIB 5 0 O033901900008 NOCOMMON 0 0 O033901900009 DATA 5 1 O033901900010 EN DATA ERR-T MISC MISC-ERR O033901900011 GEV MB MB SEE TEXT SEE TEXT O033901900012 1.1 0.39 0.12 0.22 0.07 O033901900013 ENDDATA 3 0 O033901900014 ENDSUBENT 13 0 O033901999999 SUBENT O0339020 19970516 0000O033902000001 BIB 5 5 O033902000002 REACTION (22-TI-0(P,X)12-MG-28,CUM,SIG,,,EXP) O033902000003 SAMPLE Titanium, Thickness 4.54 G/Cm**2,was Used. O033902000004 RAD-DET (12-MG-28,DG) O033902000005 DECAY-DATA (12-MG-28,20.93HR,DG,1778.8,1.) O033902000006 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033902000007 ENDBIB 5 0 O033902000008 NOCOMMON 0 0 O033902000009 DATA 5 1 O033902000010 EN DATA ERR-T MISC MISC-ERR O033902000011 GEV MB MB SEE TEXT SEE TEXT O033902000012 1.1 0.15 0.05 0.087 0.026 O033902000013 ENDDATA 3 0 O033902000014 ENDSUBENT 13 0 O033902099999 SUBENT O0339021 19970516 0000O033902100001 BIB 5 8 O033902100002 REACTION (22-TI-0(P,X)13-AL-28,IND,SIG,,,EXP) O033902100003 This Production Cross Section Could be As Independent, O033902100004 Because 28-Mg Cross Section is Less Than Uncertainty ofO033902100005 28-Al Cross Section. O033902100006 SAMPLE Titanium, Thickness 4.54 G/Cm**2,was Used. O033902100007 RAD-DET (13-AL-28,DG) O033902100008 DECAY-DATA (13-AL-28,2.24MIN,DG,1779.0,1.) O033902100009 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033902100010 ENDBIB 8 0 O033902100011 NOCOMMON 0 0 O033902100012 DATA 5 1 O033902100013 EN DATA ERR-T MISC MISC-ERR O033902100014 GEV MB MB SEE TEXT SEE TEXT O033902100015 1.1 1.02 0.28 0.58 0.16 O033902100016 ENDDATA 3 0 O033902100017 ENDSUBENT 16 0 O033902199999 SUBENT O0339022 19970516 0000O033902200001 BIB 5 5 O033902200002 REACTION (22-TI-0(P,X)12-MG-27,CUM,SIG,,,EXP) O033902200003 SAMPLE Titanium, Thickness 4.54 G/Cm**2,was Used. O033902200004 RAD-DET (12-MG-27,DG) O033902200005 DECAY-DATA (12-MG-27,9.46MIN,DG,1014.4,0.282) O033902200006 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033902200007 ENDBIB 5 0 O033902200008 NOCOMMON 0 0 O033902200009 DATA 5 1 O033902200010 EN DATA ERR-T MISC MISC-ERR O033902200011 GEV MB MB SEE TEXT SEE TEXT O033902200012 1.1 1.65 0.56 0.94 0.32 O033902200013 ENDDATA 3 0 O033902200014 ENDSUBENT 13 0 O033902299999 SUBENT O0339023 19970516 0000O033902300001 BIB 5 6 O033902300002 REACTION (22-TI-0(P,X)11-NA-24,CUM,SIG,,,EXP) O033902300003 SAMPLE Titanium, Thickness 4.54 G/Cm**2,was Used. O033902300004 RAD-DET (11-NA-24,DG) O033902300005 DECAY-DATA (11-NA-24,15.02HR,DG,1368.5,1., O033902300006 DG,2753.9,0.999) O033902300007 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033902300008 ENDBIB 6 0 O033902300009 NOCOMMON 0 0 O033902300010 DATA 5 1 O033902300011 EN DATA ERR-T MISC MISC-ERR O033902300012 GEV MB MB SEE TEXT SEE TEXT O033902300013 1.1 0.67 0.09 0.38 0.05 O033902300014 ENDDATA 3 0 O033902300015 ENDSUBENT 14 0 O033902399999 SUBENT O0339024 19970516 0000O033902400001 BIB 5 5 O033902400002 REACTION (26-FE-0(P,X)25-MN-56,CUM,SIG,,,EXP) O033902400003 SAMPLE Iron, Thickness 7.87 G/Cm**2,was Used. O033902400004 RAD-DET (25-MN-56,DG) O033902400005 DECAY-DATA (25-MN-56,2.58HR,DG,846.8,0.989) O033902400006 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033902400007 ENDBIB 5 0 O033902400008 NOCOMMON 0 0 O033902400009 DATA 5 1 O033902400010 EN DATA ERR-T MISC MISC-ERR O033902400011 GEV MB MB SEE TEXT SEE TEXT O033902400012 1.1 0.66 0.04 0.56 0.03 O033902400013 ENDDATA 3 0 O033902400014 ENDSUBENT 13 0 O033902499999 SUBENT O0339025 19970516 0000O033902500001 BIB 5 5 O033902500002 REACTION (26-FE-0(P,X)26-FE-53-G,CUM/M-,SIG,,,EXP) O033902500003 SAMPLE Iron, Thickness 7.87 G/Cm**2,was Used. O033902500004 RAD-DET (26-FE-53,DG) O033902500005 DECAY-DATA (26-FE-53,8.51MIN,DG,377.9,0.40) O033902500006 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033902500007 ENDBIB 5 0 O033902500008 NOCOMMON 0 0 O033902500009 DATA 5 1 O033902500010 EN DATA ERR-T MISC MISC-ERR O033902500011 GEV MB MB SEE TEXT SEE TEXT O033902500012 1.1 0.94 0.2 0.8 0.17 O033902500013 ENDDATA 3 0 O033902500014 ENDSUBENT 13 0 O033902599999 SUBENT O0339026 19970516 0000O033902600001 BIB 5 5 O033902600002 REACTION (26-FE-0(P,X)26-FE-53-M,CUM,SIG,,,EXP) O033902600003 SAMPLE Iron, Thickness 7.87 G/Cm**2,was Used. O033902600004 RAD-DET (26-FE-53-M,DG) O033902600005 DECAY-DATA (26-FE-53-M,2.58MIN,DG,1011.5,0.848) O033902600006 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033902600007 ENDBIB 5 0 O033902600008 NOCOMMON 0 0 O033902600009 DATA 5 1 O033902600010 EN DATA ERR-T MISC MISC-ERR O033902600011 GEV MB MB SEE TEXT SEE TEXT O033902600012 1.1 0.72 0.21 0.61 0.18 O033902600013 ENDDATA 3 0 O033902600014 ENDSUBENT 13 0 O033902699999 SUBENT O0339027 19970516 0000O033902700001 BIB 5 5 O033902700002 REACTION (26-FE-0(P,X)25-MN-52-G,CUM,SIG,,,EXP) O033902700003 SAMPLE Iron,Thickness 7.87 G/Cm**2,was Used. O033902700004 RAD-DET (25-MN-52-G,DG) O033902700005 DECAY-DATA (25-MN-52-G,5.59D,DG,935.5,0.945) O033902700006 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033902700007 ENDBIB 5 0 O033902700008 NOCOMMON 0 0 O033902700009 DATA 5 1 O033902700010 EN DATA ERR-T MISC MISC-ERR O033902700011 GEV MB MB SEE TEXT SEE TEXT O033902700012 1.1 1.22 0.22 1.04 0.19 O033902700013 ENDDATA 3 0 O033902700014 ENDSUBENT 13 0 O033902799999 SUBENT O0339028 19970516 0000O033902800001 BIB 5 8 O033902800002 REACTION (26-FE-0(P,X)25-MN-52-M,(CUM),SIG,,,EXP) O033902800003 Any Information About Possible Influence of RadioactiveO033902800004 Decay of 52-G-Fe (T1/2= 8.3 HR) Is Absent. O033902800005 SAMPLE Iron, Thickness 7.87 G/Cm**2,was Used. O033902800006 RAD-DET (25-MN-52-M,DG) O033902800007 DECAY-DATA (25-MN-52-M,21.1MIN,DG,1434.1,0.983, O033902800008 DG,744.2,0.90) O033902800009 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033902800010 ENDBIB 8 0 O033902800011 NOCOMMON 0 0 O033902800012 DATA 5 1 O033902800013 EN DATA ERR-T MISC MISC-ERR O033902800014 GEV MB MB SEE TEXT SEE TEXT O033902800015 1.1 1.04 0.09 0.88 0.08 O033902800016 ENDDATA 3 0 O033902800017 ENDSUBENT 16 0 O033902899999 SUBENT O0339029 19970516 0000O033902900001 BIB 5 5 O033902900002 REACTION (26-FE-0(P,X)24-CR-49,CUM,SIG,,,EXP) O033902900003 SAMPLE Iron,Thickness 7.87 G/Cm**2,was Used. O033902900004 RAD-DET (24-CR-49,DG) O033902900005 DECAY-DATA (24-CR-49,42.1MIN,DG,152.9,0.309) O033902900006 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033902900007 ENDBIB 5 0 O033902900008 NOCOMMON 0 0 O033902900009 DATA 5 1 O033902900010 EN DATA ERR-T MISC MISC-ERR O033902900011 GEV MB MB SEE TEXT SEE TEXT O033902900012 1.1 0.48 0.13 0.41 0.11 O033902900013 ENDDATA 3 0 O033902900014 ENDSUBENT 13 0 O033902999999 SUBENT O0339030 19970516 0000O033903000001 BIB 5 5 O033903000002 REACTION (26-FE-0(P,X)24-CR-48,CUM,SIG,,,EXP) O033903000003 SAMPLE Iron, Thickness 7.87 G/Cm**2,was Used. O033903000004 RAD-DET (24-CR-48,DG) O033903000005 DECAY-DATA (24-CR-48,22.96HR,DG,308.3,0.99) O033903000006 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033903000007 ENDBIB 5 0 O033903000008 NOCOMMON 0 0 O033903000009 DATA 5 1 O033903000010 EN DATA ERR-T MISC MISC-ERR O033903000011 GEV MB MB SEE TEXT SEE TEXT O033903000012 1.1 0.14 0.04 0.12 0.03 O033903000013 ENDDATA 3 0 O033903000014 ENDSUBENT 13 0 O033903099999 SUBENT O0339031 19970516 0000O033903100001 BIB 5 5 O033903100002 REACTION (26-FE-0(P,X)21-SC-48,,SIG,,,EXP) Independent O033903100003 RAD-DET (21-SC-48,DG) O033903100004 SAMPLE Iron, Thickness 7.87 G/Cm**2,was Used. O033903100005 DECAY-DATA (21-SC-48,1.82D,DG,1037.5,0.975) O033903100006 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033903100007 ENDBIB 5 0 O033903100008 NOCOMMON 0 0 O033903100009 DATA 5 1 O033903100010 EN DATA ERR-T MISC MISC-ERR O033903100011 GEV MB MB SEE TEXT SEE TEXT O033903100012 1.1 0.13 0.04 0.11 0.03 O033903100013 ENDDATA 3 0 O033903100014 ENDSUBENT 13 0 O033903199999 SUBENT O0339032 19970516 0000O033903200001 BIB 5 8 O033903200002 REACTION (26-FE-0(P,X)23-V-48,IND,SIG,,,EXP) O033903200003 This Production Cross Section Could be Assumed As O033903200004 Independent, Because Its Uncertainty is Less Than O033903200005 48-Cr Cross Section. O033903200006 RAD-DET (23-V-48,DG) O033903200007 SAMPLE Iron, Thickness 7.87 G/Cm**2,was Used. O033903200008 DECAY-DATA (23-V-48,15.97D,DG,983.5,1.) O033903200009 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033903200010 ENDBIB 8 0 O033903200011 NOCOMMON 0 0 O033903200012 DATA 5 1 O033903200013 EN DATA ERR-T MISC MISC-ERR O033903200014 GEV MB MB SEE TEXT SEE TEXT O033903200015 1.1 0.75 0.18 0.64 0.15 O033903200016 ENDDATA 3 0 O033903200017 ENDSUBENT 16 0 O033903299999 SUBENT O0339033 19970516 0000O033903300001 BIB 5 7 O033903300002 REACTION (26-FE-0(P,X)21-SC-47,(CUM),SIG,,,EXP) O033903300003 Any Information About Possible Influence of RadioactiveO033903300004 Decay of 47-Ca is Absent. O033903300005 RAD-DET (21-SC-47,DG) O033903300006 SAMPLE Iron, Thickness 7.87 G/Cm**2,was Used. O033903300007 DECAY-DATA (21-SC-47,3.34D,DG,159.4,0.68) O033903300008 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033903300009 ENDBIB 7 0 O033903300010 NOCOMMON 0 0 O033903300011 DATA 5 1 O033903300012 EN DATA ERR-T MISC MISC-ERR O033903300013 GEV MB MB SEE TEXT SEE TEXT O033903300014 1.1 0.78 0.15 0.66 0.13 O033903300015 ENDDATA 3 0 O033903300016 ENDSUBENT 15 0 O033903399999 SUBENT O0339034 19970516 0000O033903400001 BIB 5 5 O033903400002 REACTION (26-FE-0(P,X)21-SC-44-G,CUM/M-,SIG,,,EXP) O033903400003 RAD-DET (21-SC-44-G,DG) O033903400004 SAMPLE Iron, Thickness 7.87 G/Cm**2,was Used. O033903400005 DECAY-DATA (21-SC-44-G,3.93HR,DG,1157.,0.999) O033903400006 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033903400007 ENDBIB 5 0 O033903400008 NOCOMMON 0 0 O033903400009 DATA 5 1 O033903400010 EN DATA ERR-T MISC MISC-ERR O033903400011 GEV MB MB SEE TEXT SEE TEXT O033903400012 1.1 0.98 0.14 0.83 0.12 O033903400013 ENDDATA 3 0 O033903400014 ENDSUBENT 13 0 O033903499999 SUBENT O0339035 19970516 0000O033903500001 BIB 5 5 O033903500002 REACTION (26-FE-0(P,X)21-SC-44-M,IND,SIG,,,EXP) O033903500003 RAD-DET (21-SC-44-M,DG) O033903500004 SAMPLE Iron, Thickness 7.87 G/Cm**2,was Used. O033903500005 DECAY-DATA (21-SC-44-M,2.44D,DG,271.2,0.778) O033903500006 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033903500007 ENDBIB 5 0 O033903500008 NOCOMMON 0 0 O033903500009 DATA 5 1 O033903500010 EN DATA ERR-T MISC MISC-ERR O033903500011 GEV MB MB SEE TEXT SEE TEXT O033903500012 1.1 0.92 0.12 0.78 0.1 O033903500013 ENDDATA 3 0 O033903500014 ENDSUBENT 13 0 O033903599999 SUBENT O0339036 19970516 0000O033903600001 BIB 5 5 O033903600002 REACTION (26-FE-0(P,X)19-K-43,CUM,SIG,,,EXP) O033903600003 RAD-DET (19-K-43,DG) O033903600004 SAMPLE Iron, Thickness 7.87 G/Cm**2,was Used. O033903600005 DECAY-DATA (19-K-43,22.3HR,DG,617.5,0.783) O033903600006 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033903600007 ENDBIB 5 0 O033903600008 NOCOMMON 0 0 O033903600009 DATA 5 1 O033903600010 EN DATA ERR-T MISC MISC-ERR O033903600011 GEV MB MB SEE TEXT SEE TEXT O033903600012 1.1 0.32 0.06 0.27 0.05 O033903600013 ENDDATA 3 0 O033903600014 ENDSUBENT 13 0 O033903699999 SUBENT O0339037 19970516 0000O033903700001 BIB 5 6 O033903700002 REACTION (26-FE-0(P,X)19-K-42,IND,SIG,,,EXP) O033903700003 An Influence of 42-Ar Radioactive Decay is Negligible. O033903700004 RAD-DET (19-K-42,DG) O033903700005 SAMPLE Iron, Thickness 7.87 G/Cm**2,was Used. O033903700006 DECAY-DATA (19-K-42,12.36HR,DG,1524.6,0.183) O033903700007 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033903700008 ENDBIB 6 0 O033903700009 NOCOMMON 0 0 O033903700010 DATA 5 1 O033903700011 EN DATA ERR-T MISC MISC-ERR O033903700012 GEV MB MB SEE TEXT SEE TEXT O033903700013 1.1 0.56 0.08 0.48 0.07 O033903700014 ENDDATA 3 0 O033903700015 ENDSUBENT 14 0 O033903799999 SUBENT O0339038 19970516 0000O033903800001 BIB 5 5 O033903800002 REACTION (26-FE-0(P,X)18-AR-41,CUM,SIG,,,EXP) O033903800003 RAD-DET (18-AR-41,DG) O033903800004 SAMPLE Iron, Thickness 7.87 G/Cm**2,was Used. O033903800005 DECAY-DATA (18-AR-41,1.83HR,DG,1293.7,0.991) O033903800006 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033903800007 ENDBIB 5 0 O033903800008 NOCOMMON 0 0 O033903800009 DATA 5 1 O033903800010 EN DATA ERR-T MISC MISC-ERR O033903800011 GEV MB MB SEE TEXT SEE TEXT O033903800012 1.1 0.18 0.02 0.15 0.02 O033903800013 ENDDATA 3 0 O033903800014 ENDSUBENT 13 0 O033903899999 SUBENT O0339039 19970516 0000O033903900001 BIB 5 5 O033903900002 REACTION (26-FE-0(P,X)16-S-38,CUM,SIG,,,EXP) O033903900003 SAMPLE Iron, Thickness 7.87 G/Cm**2,was Used. O033903900004 RAD-DET (16-S-38,DG) O033903900005 DECAY-DATA (16-S-38,2.84HR,DG,1642.4,0.404) O033903900006 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033903900007 ENDBIB 5 0 O033903900008 NOCOMMON 0 0 O033903900009 DATA 5 1 O033903900010 EN DATA ERR-T MISC MISC-ERR O033903900011 GEV MB MB SEE TEXT SEE TEXT O033903900012 1.1 0.08 0.02 0.068 0.018 O033903900013 ENDDATA 3 0 O033903900014 ENDSUBENT 13 0 O033903999999 SUBENT O0339040 19970516 0000O033904000001 BIB 5 7 O033904000002 REACTION (26-FE-0(P,X)17-CL-38-G,(CUM),SIG,,,EXP) O033904000003 Ani Information About Possible Influence of RadioactiveO033904000004 Decay of 38-S is Absent. O033904000005 RAD-DET (17-CL-38-G,DG) O033904000006 SAMPLE Iron, Thickness 7.87 G/Cm**2,was Used. O033904000007 DECAY-DATA (17-CL-38-G,37.24MIN,DG,1642.4,0.316) O033904000008 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033904000009 ENDBIB 7 0 O033904000010 NOCOMMON 0 0 O033904000011 DATA 5 1 O033904000012 EN DATA ERR-T MISC MISC-ERR O033904000013 GEV MB MB SEE TEXT SEE TEXT O033904000014 1.1 0.058 0.023 0.05 0.02 O033904000015 ENDDATA 3 0 O033904000016 ENDSUBENT 15 0 O033904099999 SUBENT O0339041 19970516 0000O033904100001 BIB 5 6 O033904100002 REACTION (26-FE-0(P,X)11-NA-24,,SIG,,,EXP) O033904100003 RAD-DET (11-NA-24,DG) O033904100004 SAMPLE Iron,Thickness 7.87 G/Cm**2,was Used. O033904100005 DECAY-DATA (11-NA-24,15.02HR,DG,1368.5,1., O033904100006 DG,2753.9,0.999) O033904100007 ERR-ANALYS (ERR-T).The Uncertainty was Recalculated by Compiler. O033904100008 ENDBIB 6 0 O033904100009 NOCOMMON 0 0 O033904100010 DATA 5 1 O033904100011 EN DATA ERR-T MISC MISC-ERR O033904100012 GEV MB MB SEE TEXT SEE TEXT O033904100013 1.1 0.13 0.02 0.11 0.02 O033904100014 ENDDATA 3 0 O033904100015 ENDSUBENT 14 0 O033904199999 ENDENTRY 41 0 O033999999999